Large parts of banks of canals in the Netherlands are protected by azobé timber sheet piles. Many kilometers of sheet piles in the province of Noord-Holland, are planned to be replaced or to undergo maintenance. Yet, there is insufficient knowledge on the current state of the azobé sheet piles and their residual service life. Based on this, a series of investigations on azobé sheet piles after 57 years of service were performed. Visual inspections showed surface deterioration on the water-exposed side for all boards. Nondestructive testing using micro drilling technique showed no signs of internal deterioration. A maximum reduction in thickness of 17% and an average thickness reduction of 6.7% of original thickness were observed. CT scanning showed that the remaining cross sections of the azobé boards were intact and had comparable density of new azobé boards. An exponential damage accumulation model was used to predict the residuals service life of the timber sheet piles subjected to earth stress. Conservative estimates based on physical measurements and residual bending strength indicate that the sheet piles have an additional service life of 22–43 years from the current state.
A study on deterioration and residual service life of recovered azobé (Lophira alata) sheet piles
Mirra, MicheleSecondo
;
2025-01-01
Abstract
Large parts of banks of canals in the Netherlands are protected by azobé timber sheet piles. Many kilometers of sheet piles in the province of Noord-Holland, are planned to be replaced or to undergo maintenance. Yet, there is insufficient knowledge on the current state of the azobé sheet piles and their residual service life. Based on this, a series of investigations on azobé sheet piles after 57 years of service were performed. Visual inspections showed surface deterioration on the water-exposed side for all boards. Nondestructive testing using micro drilling technique showed no signs of internal deterioration. A maximum reduction in thickness of 17% and an average thickness reduction of 6.7% of original thickness were observed. CT scanning showed that the remaining cross sections of the azobé boards were intact and had comparable density of new azobé boards. An exponential damage accumulation model was used to predict the residuals service life of the timber sheet piles subjected to earth stress. Conservative estimates based on physical measurements and residual bending strength indicate that the sheet piles have an additional service life of 22–43 years from the current state.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.