We studied the oxidation state of Fe in silicate glasses produced during the first atomic bomb blast at the Trinity test site (New Mexico) by X-ray absorption–near edge spectroscopy (XANES). The sample consists of green glass resulting from melting of the quartz-bearing sand present at the test site; some relict unmelted sand is still fused to the bottom of the sample. Comparison of the pre-edge peak data with model compounds of known Fe oxidation state and coordination number shows that in the Trinity glass sample, Fe is in the divalent state and, on average, in a mixture of 4- and 5-fold coordination. XANES spectra collected at various heights of the sample, from the bottom of the sample up to the exposed surface, show no variation of the pre-edge peak and, thus, of the Fe oxidation state with the distance from the sandglass interface. However, XANES analysis of a portion of the sand at the bottom of the sample shows Fe to be a mixture of Fe2+ and Fe3+, with a Fe3+/(Fe2+ + Fe3+) ratio close to 0.5. This demonstrates that during the nuclear explosion, the ground rock was instantaneously reduced, transforming all the iron from mostly trivalent state to almost exclusively divalent.

Iron reduction in silicate glass produced during the 1945 nuclear test at the Trinity site (Alamogordo, New Mexico, USA).

GIULI, Gabriele;PARIS, Eleonora
2010-01-01

Abstract

We studied the oxidation state of Fe in silicate glasses produced during the first atomic bomb blast at the Trinity test site (New Mexico) by X-ray absorption–near edge spectroscopy (XANES). The sample consists of green glass resulting from melting of the quartz-bearing sand present at the test site; some relict unmelted sand is still fused to the bottom of the sample. Comparison of the pre-edge peak data with model compounds of known Fe oxidation state and coordination number shows that in the Trinity glass sample, Fe is in the divalent state and, on average, in a mixture of 4- and 5-fold coordination. XANES spectra collected at various heights of the sample, from the bottom of the sample up to the exposed surface, show no variation of the pre-edge peak and, thus, of the Fe oxidation state with the distance from the sandglass interface. However, XANES analysis of a portion of the sand at the bottom of the sample shows Fe to be a mixture of Fe2+ and Fe3+, with a Fe3+/(Fe2+ + Fe3+) ratio close to 0.5. This demonstrates that during the nuclear explosion, the ground rock was instantaneously reduced, transforming all the iron from mostly trivalent state to almost exclusively divalent.
2010
9780813724652
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11581/109909
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 19
  • ???jsp.display-item.citation.isi??? ND
social impact